Journal of Manufacturing and Materials Processing doi: 10.3390/jmmp8020082

Authors: Keita Marumoto Akira Fujinaga Takeshi Takahashi Hikaru Yamamoto Motomichi Yamamoto

This study presents a new gas metal arc welding (GMAW) technique that achieves both high efficiency and low heat input using a hybridization of the hot-wire method. The optimal combination of welding speed and welding current conditions was investigated using a fixed hot-wire feeding speed of 10 m/min on a butt joint with a V-shaped groove using 19 mm thick steel plates. Molten pool stability and defect formation were observed using high-speed imaging and cross-sectional observations. The power consumption and heat input were predicted prior to welding and measured in the experiments. The results indicate that a combination of a welding current of 350–500 A and welding speed of 0.3–0.7 m/min is optimal to avoid defect formation and molten metal precedence using three or four passes. The higher efficiency and lower heat input achieved by hot-wire GMAW results in a weld metal of adequate hardness, narrower heat-affected zone, smaller grain size at the fusion boundary, and lower power consumption than those obtained using tandem GMAW and high-current GMAW. Based on the experimental results, a single bevel groove, which is widely used in construction machinery welding joints, was welded using hot-wire GMAW, and we confirmed that the welding part could be welded in six passes, whereas eight passes were required with GMAW only.