Materials, Vol. 17, Pages 405: Composition and Surface Optical Properties of GaSe:Eu Crystals before and after Heat Treatment

Materials, Vol. 17, Pages 405: Composition and Surface Optical Properties of GaSe:Eu Crystals before and after Heat Treatment

Materials doi: 10.3390/ma17020405

Authors: Veaceslav Sprincean Haoyi Qiu Tim Tjardts Oleg Lupan Dumitru Untilă Cenk Aktas Rainer Adelung Liviu Leontie Aurelian Carlescu Silviu Gurlui Mihail Caraman

This work studies the technological preparation conditions, morphology, structural characteristics and elemental composition, and optical and photoluminescent properties of GaSe single crystals and Eu-doped β–Ga2O3 nanoformations on ε–GaSe:Eu single crystal substrate, obtained by heat treatment at 750–900 °C, with a duration from 30 min to 12 h, in water vapor-enriched atmosphere, of GaSe plates doped with 0.02–3.00 at. % Eu. The defects on the (0001) surface of GaSe:Eu plates serve as nucleation centers of β–Ga2O3:Eu crystallites. For 0.02 at. % Eu doping, the fundamental absorption edge of GaSe:Eu crystals at room temperature is formed by n = 1 direct excitons, while at 3.00 at. % doping, Eu completely shields the electron–hole bonds. The band gap of nanostructured β–Ga2O3:Eu layer, determined from diffuse reflectance spectra, depends on the dopant concentration and ranges from 4.64 eV to 4.87 eV, for 3.00 and 0.05 at. % doping, respectively. At 0.02 at. % doping level, the PL spectrum of ε–GaSe:Eu single crystals consists of the n = 1 exciton band, together with the impurity band with a maximum intensity at 800 nm. Fabry–Perrot cavities with a width of 9.3 μm are formed in these single crystals, which determine the interference structure of the impurity PL band. At 1.00–3.00 at. % Eu concentrations, the PL spectra of GaSe:Eu single crystals and β–Ga2O3:Eu nanowire/nanolamellae layers are determined by electronic transitions of Eu2+ and Eu3+ ions.