Metals, Vol. 13, Pages 1905: Microstructure and Magnetism of Heavily Helium-Ion Irradiated Epitaxial Iron Films

Metals, Vol. 13, Pages 1905: Microstructure and Magnetism of Heavily Helium-Ion Irradiated Epitaxial Iron Films

Metals doi: 10.3390/met13111905

Authors: Yasuhiro Kamada Daiki Umeyama Tomoki Oyake Takeshi Murakami Kazuyuki Shimizu Satomi Fujisaki Noriyuki Yoshimoto Kazuhito Ohsawa Hideo Watanabe

This study reports on the microstructure and magnetism of pure iron irradiated with high doses of helium ions. Iron alloys are important structural materials used as components in fusion reactors, and a comprehensive database of their various properties has been developed. But little has been investigated on magnetic properties, in particular, the effects of high doses and helium cavities are lacking. Single-crystal iron films, with a thickness of 200 nm, were prepared using the ultra-high vacuum evaporation method. These films were then irradiated with 30 keV He+ ions at room temperature up to a dose of 18 dpa. X-ray diffraction measurements and cross-sectional transmission electron microscope observations revealed significant microstructural changes, including a large lattice expansion perpendicular to the film plane and the formation of high-density cavities after irradiation. However, the saturation magnetization and the shape of the magnetization curve showed almost no change, indicating the robustness of the magnetic properties of iron.