Surfaces, Vol. 6, Pages 53-63: In Situ Gas-Phase Polymerization of Polypyrrole-Coated Lithium-Rich Nanotubes for High-Performance Lithium-Ion Batteries

Surfaces, Vol. 6, Pages 53-63: In Situ Gas-Phase Polymerization of Polypyrrole-Coated Lithium-Rich Nanotubes for High-Performance Lithium-Ion Batteries

Surfaces doi: 10.3390/surfaces6010005

Authors: Yangwen Chen Beibei Sun Xinchang Wang Junmin Xu Liwei Zhang Jipeng Cheng

Conductive polymer polypyrrole (PPy)-coated lithium-rich manganese-based Li1.2Mn0.54Ni0.13Co0.13O2 (LMNCO) nanotube cathode materials were synthesized by electrospinning and subsequently subjected to low-temperature vapor-phase polymerization. X-ray diffraction (XRD), scanning electron microscopy (SEM) and high-resolution transmission electron microscopy (HRTEM) results confirm that the successful coating of the PPy layer (~2 nm) on the surface of LMNCO nanotubes did not destroy their morphologies or structures. Electrochemical tests indicate that the electrochemical performance of PPy-coated LMNCO nanotubes has been significantly enhanced. At a rate of 1 C, the discharge capacity of the PPy-coated LMNCO cell is 200.1 mAh g−1, and the capacity retention is 99% after 120 cycles. This excellent stability is attributed to the inhibition of side reactions and the protective function of the tubular structure due to the PPy coating layer. Additionally, the rate capability is also improved at a high current density due to the higher electronic and ionic conductivity.